PVC Paste Resin PB1702 For Automotive Decoration Materials

$1700

≥5
Metric Ton

Payment Type:

L/C,T/T,Paypal,Money Gram,Western Union

Incoterm:

FOB,CFR,CIF,EXW,FCA,CPT,CIP

Min. Order:

5 Metric Ton

Transportation:

Ocean,Land,Air

Port:

Qingdao,Tianjin,Shanghai

Contact Now

Product Description

Product Attributes
Supply Ability & Additional Information
Packaging & Delivery

< >

Overview

Product Attributes

Model No.: PB1702,PB1302.P440,P450

Brand: Shenfeng

Supply Ability & Additional Information

Packaging: 20kgs bag

Productivity: 18000TON/MONTH

Transportation: Ocean,Land,Air

Place of Origin: CHINA

Supply Ability: 18000TON/MONTH

Certificate: ISO,CIQ,SGS

HS Code: 39041090

Port: Qingdao,Tianjin,Shanghai

Payment Type: L/C,T/T,Paypal,Money Gram,Western Union

Incoterm: FOB,CFR,CIF,EXW,FCA,CPT,CIP

Packaging & Delivery

Selling Units:: Metric Ton

Package Type:: 20kgs bag

PVC Paste Resin PB1702 For Automotive Decoration Materials

Property：

The emulsion polymerization formula mainly includes VCM, water, water-soluble initiator and emulsifier. Emulsion polymerization has strict requirements for stirring. The initiation is carried out in the water phase. The initiator usually used is water-soluble persulfate. In general, the particle size of the latex obtained by emulsion polymerization is less than 0.2μm. In order to achieve the purpose of increasing the particle size of the latex, the emulsion seed polymerization method was developed to increase the particle size of the latex to about 1.0μm. In emulsion polymerization, if there is a high polymer latex that has been formed, control the material ratio and conditions, in principle, VCM only polymerizes on the latex particles that have been generated, and no new particles are formed; this kind of high polymer Polymer latex is like seed, so it is called "emulsion seed polymerization". However, only a reasonable particle size is not enough. It must have a proper particle size distribution to obtain a PVC paste Resin with excellent performance. The emulsifier is very important in emulsion polymerization. The amount used determines the number of initiator particles and plays a major role in the size of the final latex particles. Especially during seed production, the use of high initiation rate and low concentration of emulsifier for production can narrow the size distribution of latex particles.

Specification

Test items		SPECIFICATION
Test items		PB1152	PB1202	PB1302	PB1702	PB1311
Viscosity,ml/g		100-120	100-120	115-135	153-173	115-135
K value		68	68	70	79	70
degree of polymerization		900-1500	900-1150	1100-1350	1700-1950	1100-1350
surface density,g/cm3		0.30-0.45	0.30-0.45	0.30-0.45	0.30-0.45	0.30-0.45
heat loss,%<		0.4	0.4	0.4	0.4	0.4
average grain diameter,um		15+/-5	15+/-5	15+/-5	15+/-5	15+/-5
>90um		0	0	0	0	0
>50um		1	1	1	1	1
VCM vestigital,mg/kg<		5	5	5	5	5
plastipaste PVC,DOP		100:100	100:60	100:60	100:60	100:100
PVC:DOP		100:50	100:50	100:50	100:50	100:100
Brinell viscosityPa.s	2hrs	6	3.0-7.0	3.0-7.0	3.0-7.0	20-50
Brinell viscosityPa.s	24hrs	10	3.0-10	3.0-10	3.0-10	60-100
West Speed g/s		Φ3.8mm，L=50mm，2hrs
0.4Mpa		>2.4	>3.2	>3.2	>3.2	>2
0.8Mpa		>5	>8	>8	>8	>4

Application
PVC Paste Resin is mainly used in soft materials field of PVC products,it can be applied to coating,impregnating,spraying,foaming and other processing technics,widely used in the production of artificial leather,decorative materials,floor leather,wall paper,industrial belt,sports venues,coatings,adhesives,toys,medical disposable gloves,household decoration materials,electrical instrumentation and electrical tools and other materials and products.