Polyvinyl Alcohol PVA 1799 For Building Mortar
Polyvinyl Alcohol 1788 has good chemical stability, good insulation and film-forming properties. With the typical chemical properties of polyols, it can carry out reactions such as esterification, etherification and acetalization. In addition, it also has the following performance:
(1) Water-soluble
Storage stability of polyvinyl alcohol 1788 aqueous solution The polyvinyl alcohol aqueous solution has little chemical change when stored for a long time. At room temperature, the viscosity will gradually increase with the extension of the standing time; it will turn into a gel at low temperature, and it will turn into a solution after heating and stirring. If it is placed for a long time, rust inhibitor, preservative, anti-gelling agent and viscosity stabilizer can be added to the solution. However, attention should be paid to the influence of additives on product quality and performance during use.
(2) Film-forming properties
PVA1788 is easy to form film, and its film has excellent mechanical properties. The tensile strength of the film increases with the increase of polymerization degree and alcoholysis degree.
(3) Adhesion
The aqueous solution of polyvinyl alcohol 1788 has good bonding force with hydrophilic cellulose, and the bonding strength increases with the increase of alcoholysis degree and polymerization degree.
(4) Chemical properties of the interface
Polyvinyl alcohol 088-20 (1788) is surface active and reduces the surface tension of water.
(5) Solvent resistance
Polyvinyl Alcohol 088-20 (1788) can be dissolved in polar solution containing hydroxyl group, but it is easy to transform into gel, generally insoluble in non-polar organic solution, and insoluble in inorganic ACID , water is a good solvent.
(6) Thermal stability
Polyvinyl alcohol 088-20 (1788) has good thermal stability and does not change at temperatures below 140 degrees.
Discription:
Chuanwei polyvinyl alcohol 088-20 Resin series products are white solids with three types of flocculent, granular and powdery appearances; odorless and soluble in water at 80--90 °C. Its aqueous solution has good adhesion and film-forming properties; it is resistant to most organic solvents such as oils, lubricants and hydrocarbons; it has chemical properties such as esterification, etherification, and acetalization of long-chain polyols.
Specification:
| Items | Degree of alcoholysis (Mol)% | viscosity (mPa.s) | Volatile content % ≤ | ash content % ≤ | pH | Purity % ≥ |
| 100-27S | 99.5～100.0 | 23.0～29.0 | 6.0 | 0.8 | - | 92.0 |
| 100-40 | 99.5～100.0 | 35.0～45.0 | 6.0 | 0.8 | - | 92.0 |
| 100-78 | 99.5～100.0 | 73.0～83.0 | 6.0 | 0.8 | - | 92.0 |
| 098-03 | 98.0～98.8 | 3.2～4.0 | 5.0 | 0.7 | 5.0～7.0 | 94.0 |
| 098-04 | 98.0～98.8 | 4.0～5.0 | 5.0 | 0.5 | 5.0～7.0 | 94.0 |
| 098-10 | 98.0～98.8 | 8.0～12.0 | 5.0 | 0.5 | 5.0～7.0 | 94.0 |
| 098-15 | 98.0～98.8 | 13.0～17.0 | 5.0 | 0.5 | 5.0～7.0 | 94.0 |
| 098-20 | 98.0～98.8 | 18.0～22.0 | 5.0 | 0.5 | 5.0～7.0 | 94.0 |
| 098-27 | 98.0～98.8 | 23.0～29.0 | 5.0 | 0.5 | 5.0～7.0 | 94.0 |
| 098-30 | 98.0～98.8 | 28.0～32.0 | 5.0 | 0.5 | 5.0～7.0 | 94.0 |
| 097-29 | 96.0～98.0 | 27.0～31.0 | 5.0 | 0.5 | 5.0～7.0 | 94.0 |
| 097-60 | 96.0～98.0 | 56.0～66.0 | 5.0 | 0.5 | 5.0～7.0 | 94.0 |
| 092-53 | 91.0～93.0 | 48.0～58.0 | 5.0 | 0.5 | 5.0～7.0 | 94.0 |
| 088-03 | 86.5～88.5 | 3.0～4.0 | 5.0 | 0.7 | 5.0～7.0 | 94.0 |
| 088-05 | 86.5～88.5 | 4.5～6.0 | 5.0 | 0.5 | 5.0～7.0 | 94.0 |
| 088-08 | 86.5～88.5 | 8.0～10.0 | 5.0 | 0.5 | 5.0～7.0 | 94.0 |
| 088-13 | 86.5～88.5 | 12.0～14.0 | 5.0 | 0.5 | 5.0～7.0 | 94.0 |
| 088-20 | 86.5～88.5 | 21.0～24.5 | 5.0 | 0.4 | 5.0～7.0 | 94.0 |
| 088-26 | 86.5～88.5 | 24.0～28.0 | 5.0 | 0.5 | 5.0～7.0 | 94.0 |
| 088-35 | 86.5～88.5 | 29.0～34.0 | 5.0 | 0.3 | 5.0～7.0 | 94.0 |
| 088-40 | 86.5～88.5 | 38.0～42.0 | 5.0 | 0.5 | 5.0～7.0 | 94.0 |
| 088-50 | 86.5～88.5 | 45.0～55.0 | 5.0 | 0.3 | 5.0～7.0 | 94.0 |
| 080-44 | 78.0～82.0 | 42.0～52.0 | 5.0 | 0.5 | 5.0～7.0 | 94.0 |
| 088-60 | 86.5～88.5 | 56.0～66.0 | 5.0 | 0.5 | 5.0～7.0 | 94.0 |
| 086-03 | 85.0～87.0 | 3.4～4.2 | 5.0 | 0.4 | 5～7 | 93.5 |
| 098-05 | 98.0～99.0 | 5.0～6.5 | 5.0 | 0.5 | 5～7 | 93.5 |
| 098-08 | 98.0～99.0 | 9.0～11.0 | 5.0 | 0.5 | 5～7 | 93.5 |
| 092-20 | 91.0～93.0 | 21.0～27.0 | 5.0 | 0.5 | 5～7 | 93.5 |
| 094-27 | 94.0～96.0 | 22.0～28.0 | 5.0 | 0.5 | 5～7 | 93.5 |
| 096-27 | 96.0～98.0 | 23.0～29.0 | 5.0 | 0.5 | 5～7 | 93.5 |
| 100-27 | 99.0～100.0 | 22.0～28.0 | 5.0 | 0.7 | / | 93.5 |
| 092-35 | 91.0～93.0 | 30.0～36.0 | 5.0 | 0.3 | 5～7 | 93.5 |
| 100-35 | 99.0～100.0 | 35.0～43.0 | 5.0 | 0.7 | 5～7 | 93.5 |
| 098-60 | 98.0～99.0 | 58.0～68.0 | 5.0 | 0.5 | 5～7 | 93.5 |
| 100-60 | 99.0～100.0 | 58.0～68.0 | 5.0 | 0.7 | 5～7 | 93.5 |
| 100-70 | 99.0～100.0 | 68.0～78.0 | 5.0 | 0.7 | 5～7 | 93.5 |
Packing:
paper-plastic composite bag, with plastic film inner bag, net weight of each bag is 20kg&25kg.
Application:
Mainly used in textile pulp, paper binder, rewetting binder, surface sizing agent for paper, pigment carrier, Adhesives for architectural coatings, adhesives and additives for building materials, coating agents for seeds and pharmaceuticals, adhesives for inorganic and electronic products, Water-soluble film, cosmetic additive, stabilizer for vinyl acetate emulsion polymerization and vinyl chloride suspension polymerization, temporary protective film etc.